# gst: monitoring of stable crack growth; crack tip behavior at the nanoscale (during ceramic fracture).

<< To understand fracture and make brittle materials more ductile, (AA) rely on modeling what happens at a crack tip. However, observing a crack tip in a brittle material is challenging: cracks propagate fast, and the events that (AA) are interested in observing occur at the nanoscale or below. Up to now, (They) were not able to observe what happens ahead of a moving crack tip. >>

<< In this work, (AA) show how by carefully performing fracture experiments inside a transmission electron microscope (They) can grow stable cracks while observing the nanoscale events happening at the crack tip. >>️

Oriol Gavalda-Diaz, Max Emmanuel, et al. Observing the crack tip behavior at the nanoscale during fracture of ceramics. PNAS. 121 (43) e2408292121. Oct 17, 2024.

https://www.pnas.org/doi/10.1073/pnas.2408292121 